Fabricating method of packaging structure

ABSTRACT

A fabricating method of packaging structure is provided. First, a capacitive element is formed. Then, a first dielectric layer is formed on a first electronic component by performing a build-up process, an interconnection is formed in the first dielectric layer, and a plurality of contacts are formed on the upper and lower surfaces of the first dielectric layer, wherein the capacitive element is embedded in the first dielectric layer during the fabrication of the interconnection and the capacitive element is electrically connected to the corresponding contacts through the interconnection. A second electronic component is disposed on the first dielectric layer, wherein the second electronic component is electrically connected to the corresponding contacts.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a divisional application of and claims priority benefit of U.S. application Ser. No. 11/733,783, filed Apr. 11, 2007, now allowed, which claims the priority benefit of Taiwan application serial no. 95133410, filed Sep. 11, 2006. The entirety of each of the above-mentioned patent applications is hereby incorporated by reference herein and made a part of this specification.

BACKGROUND

1. Technical Field

The disclosure relates to a semiconductor manufacturing method thereof. More particularly, the disclosure relates to a packaging structure manufacturing method.

2. Technical Art

The technology of stacking chips can shorten the transmission pathway of electronic signals and provide an efficient technique to integrate different material chips. In terms of the latter, it can stack up the high-frequency power amplifier chips and radio frequency chips, or can be integrated with the micro-electro mechanical system devices. Moreover, the overall performance of the stacked-chip packaging structure can be improved if the passive elements can be integrated effectively. Therefore, it is essential to provide a high quality and highly integrated interposer structure with passive elements between the stacked chips.

Referring to FIG. 1, it is a schematic view of a conventional stacked circuit device. The conventional stacked circuit device 100 is disclosed in U.S. Pat. No. 6,661,088, wherein it includes a chip 110, an interposer structure 120 and a substrate 130. A plurality of pads 112 disposed on the chip 110 is electrically connected to the corresponding multiple pads 132 disposed on the substrate 130 through the interposer structure 120. The main purpose of the interposer structure 120 is to serve as circuit redistribution.

Another conventional stacked circuit device is provided for the purpose of integrating different type circuit elements such as active elements and passive elements to the interposer structure. Referring to FIG. 2, it is a schematic view of another conventional stacked circuit device. The conventional stacked circuit device 200 disclosed in U.S. Pat. No. 6,614,106 includes a chip 210, an interposer structure 220 and a base substrate 230. It should be noted that for the sake of clarified description, FIG. 2 also shows the enlarged view of the interposer structure 220. A plurality of terminals 212 of the chip 210 are electrically connected to the corresponding multiple terminals 222 of the interposer structure 220. Whereas the other terminals 224 of the interposer structure 220 are electrically connected to the set of terminals of the base substrate 230. The interposer structure 220 comprises an insulating film 226, a semiconductor substrate 228, and a plurality of circuit elements 229 such as the active and passive elements which are disposed in the insulating film 222.

Other related techniques of fabricating passive elements on the semiconductor base material of the interposer structure are disclosed in U.S. Pat. Nos. 6,500,724, 6,819,001 and 6,274,937. However, fabricating passive elements on the semiconductor base material may leads to low quality factor of inductive elements, inferior capacitance due to the limitations of material and processing temperature of semiconductor, and poor resistance of the resistive elements.

To overcome the aforementioned drawbacks, the method of fabricating passive elements on the insulating materials, ceramic or plastic, of the interposer structure are proposed and the related techniques are described in the U.S. Pat. Nos. 6,933,601, 6,611,419 and 5,530,288. However, it often cost much since to fabricate inductive elements on ceramic base substrate, the high priced material, silver, is often used. On the other hand, the quality factor of the inductive elements is decreased while adopting epoxy resin as the dielectric material to fabricate the inductive element on a plastic substrate. In addition, it may cause poor capacitance when fabricating capacitive elements on the insulating substrate, less process compatibility when manufacturing resistive elements on the ceramic substrate, and unstable resistance when forming the resistive elements on the plastic substrate. Also, it may make the final product of the interposer structure big and thick when fabricating passive elements on the insulating base materials.

SUMMARY

The embodiment is directed to a fabricating method of packaging structure, which comprises: forming a capacitive element; forming a first dielectric layer on a first electronic component by performing a build-up process, forming an interconnection in the first dielectric layer, and forming a plurality of contacts on the upper and lower surfaces of the first dielectric layer, wherein the capacitive element is embedded in the first dielectric layer during the fabrication of the interconnection and the capacitive element is electrically connected to the corresponding contacts through the interconnection; and, disposing a second electronic component on the first dielectric layer, wherein the second electronic component is electrically connected to the corresponding contacts.

According to an embodiment, the fabricating method of the packaging structure further comprises forming an inductive element at the same time of fabricating the interconnection and the inductive element is electrically connected to the corresponding contacts through the interconnection. Further, the inductive element may be disposed surrounding the capacitive element.

According to an embodiment, the fabricating method of the packaging structure may further comprise performing a thermal treatment process to the dielectric material after coating the same.

According to an embodiment, the fabricating method of the packaging structure may further comprise forming a barrier layer on the metal film before coating the dielectric material.

According to an embodiment, the fabricating method of the packaging structure may further comprise performing an etching process to the capacitive element to define the surface area thereof after the capacitive element is embedded into the first dielectric layer.

According to an embodiment, the fabricating method of the packaging structure further comprises providing a resistive module at the same time of fabricating the interconnection, and making the resistive module and the capacitive element stacked up with each other and to be embedded into the first dielectric layer, wherein the resistive module is electrically connected to the corresponding contacts through the interconnection.

According to an embodiment, the capacitive element and the aforementioned resistive module may be stacked up with each other first, and then being embedded into the first dielectric layer together.

According to an embodiment, the resistive module can be fabricated by: providing a substrate and forming a resistive thin film thereon. In addition, the steps of fabricating the resistive module may further include: forming a plurality of electrodes on the substrate, wherein the resistive thin film is electrically connected with the electrodes; and, forming a passivation layer on the substrate to cover the electrodes and the resistive thin film.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings are included to provide a further understanding of the embodiment, and are incorporated in and constitute a part of this specification. The drawings illustrate embodiments and, together with the description, serve to explain the principles of the embodiment.

FIG. 1 is a schematic view of a conventional stacked circuit device.

FIG. 2 is a schematic view of another conventional stacked circuit device.

FIG. 3 is a schematic view showing a packaging structure according to an embodiment.

FIG. 4 is a flow chart showing the steps of fabricating a packaging structure according to an embodiment.

FIGS. 5A to 5C are cross-sectional views schematically illustrating the steps of fabricating a packaging structure according to an embodiment.

FIGS. 6A to 6F are cross-sectional views schematically showing a fabricating process of a capacitive element.

FIGS. 7A to 7C are cross-sectional views schematically showing a fabricating process of the interposer structure shown in FIG. 5B.

FIG. 8 is a flow chart illustrating a fabricating method of a packaging structure according to another embodiment.

FIG. 9 is a cross-sectional view schematically illustrating the steps S020′ shown in FIG. 8.

FIGS. 10A to 10B are cross-sectional views schematically showing a fabricating process of the resistive module shown in FIG. 9.

FIG. 11 is a flow chart illustrating a fabricating method of a packaging structure according to another embodiment.

FIG. 12 is a cross-sectional view schematically showing the steps S020″ shown in FIG. 11.

DESCRIPTION OF EMBODIMENTS

Reference will now be made in detail to the embodiments, examples of which are illustrated in the accompanying drawings. Wherever possible, the same reference numbers are used in the drawings and the description to refer to the same or like parts.

Referring to FIG. 3, a cross sectional view showing a packaging structure according to an embodiment is illustrated. A packaging structure 300 includes an interposer structure 310, a first electronic component 320 and a second electronic component 330, wherein the first electronic component 320 and a second electronic component 330 can be either semiconductor chip or wafer. The interposer structure 310 includes a first dielectric layer 311, a plurality of contacts 312, a capacitive element 313, an inductive element 314 and an interconnection 315. The contacts 312 are disposed on the upper surface 311 a and lower surface 311 b of the first dielectric layer 311. The capacitive element 313 is embedded into the first dielectric layer 311. And, the capacitive element 313 comprises two conductive layers 313 a and a second dielectric layer 313 b located between the conductive layers 313 a. The inductive element 314 and the interconnection 315 are embedded into the first dielectric layer 311. The capacitive element 313 and the inductive element 314 are electrically connected to the corresponding contacts 312 through the interconnection 315. The first electronic component 320 and the second electronic component 330 are respectively disposed on the upper and lower sides of the interposer structure 310 and electrically connected to the corresponding contacts 312.

In the embodiment, the permittivity of the first dielectric layer 311 is smaller than that of the second dielectric layer 313 b. Since the permittivity of the second dielectric layer 313 b of the capacitive element 313 is higher, a higher capacitance value of the capacitive element 313 can be attained. On the other hand, since the permittivity of the first dielectric layer 311 is lower, the parasitic capacitance of the inductive element 314 is lower and thus has a better Q-factor. When being as a decoupling capacitor, the efficiency of the capacitive element 313 can be improved by arranging the capacitive element 313 near by the first electronic component 320 and the second electronic component 330, according to the necessity of the design.

In the embodiment, the spiral-like inductive element 314 can be disposed surrounding the capacitive element 313, resulting the high integration density of the passive element of the interposer structure 310, thus the interposer structure 310 is thinner and smaller in size. In addition, the capacitive element 313 further includes a barrier layer 313 c, which is disposed between one of the conductive layers 313 a and the second dielectric layer 313 b. The material of the barrier layer 313 c includes titanium (Ti), platinum (Pt), or silver (Ag). The barrier layer 313 c can prevent the conductive layers 313 a from reacting with the second dielectric layer 313 b when fabricating the capacitive element 313. The material of the second dielectric layer 313 b located at the capacitive element 313 includes ceramic, such as the ferroelectric materials of barium titanate (BaTiO3) or strontium titanate (SrTiO3); and the material of the first dielectric layer 311 includes benzocyclobutene (BCB) or polyimide (PI).

Referring to FIG. 3, the interposer structure 310 further includes a resistive module 316, which is embedded into the first dielectric layer 311 and stacked up with the capacitive element 313. According to the relative position shown in FIG. 3, the capacitive element 313 can be stacked up on the resistive module 316, and the resistive module 316 is electrically connected to the corresponding contacts 312 through the interconnection 315. The resistive module 316 includes a substrate 316 a, which can be made of ceramic, and a resistive film 316 b. The resistive film 316 b is disposed on the substrate 316 a and electrically connected to the interconnection 315. Moreover, the resistive module 316 includes a plurality of electrodes 316 c and a passivation layer 316 d. The electrodes 316 c are disposed on the substrate 316 a and the resistive film 316 b is connected to the interconnection 315 via the electrodes 316 c. The passivation layer 316 d is disposed on the substrate 316 a and covers the resistive film 316 b and the electrodes 316 c.

It should be noted that even though the interposer structure 310 of the above embodiment, comprises of the capacitive element 313, the inductive element 314 and resistive module 316 for an example. In another embodiment, the interposer structure 310 may only contain the capacitive element 313 for serving as de-coupling capacitors. Therefore, the efficiency of the capacitive element 313, which serves as a decoupling capacitor, can be improved by arranging the capacitive element 313 near by the first electronic component 320 and the second electronic component 330.

The following is a detailed description of a fabricating method of a packaging structure according to an embodiment. FIG. 4 is a flow chart showing the steps of fabricating the packaging structure. FIGS. 5A to 5C are cross-sectional views schematically illustrating the steps of fabricating the packaging structure. The fabricating method of the packaging structure of the embodiment includes the steps S010, S020 and S030. Referring to FIGS. 4 and 5A, first of all, the step S010 is carried out to form the capacitive element 313.

FIGS. 6A to 6F are cross-sectional views schematically showing a fabricating process of the capacitive element shown in FIG. 5A. The fabricating method of the capacitive element 313 includes the following sub-steps. First, referring to FIG. 6A, a metal film M is provided. Next, referring to FIG. 6B, a barrier layer 313 c can be formed on the metal film M to prevent the reaction of the metal film M with the dielectric material D formed in the following steps and thus preserve the dielectric characteristic of the dielectric material D if the metal film M will react with the dielectric material D. Referring to FIG. 6C, a dielectric material D, such as a suspended ceramic slurry, is coated on the metal film M, wherein the ceramic slurry can be prepared from the nanometer ferroelectric material powder by performing the sol-gel method. Then, referring to FIG. 6D, the manufacturing process of, for example, a thermal treatment, such as annealing, is performed to the dielectric material D. Referring to FIG. 6E, an electrode layer E is formed on the dielectric material D to finish the basic manufacture of the capacitive element 313. After that, referring to the FIG. 6F, the finished capacitive element 313 can be trimmed into a size. Referring to FIG. 6F, the trimmed capacitive element 313 comprises two conductive layers 313 a, a second dielectric layer 313 b located among the conductive layers 313 a, and a barrier layer 313 c disposed between the second dielectric layer 313 b and one of the conductive layers 313 a.

Then, referring to FIGS. 4 and 5B, an interposer structure 310 is formed through the steps S020, wherein a first dielectric layer 311 is formed on a first electronic component 320 through the build-up process. An inductive element 314 and an interconnection 315 are fabricated in the first dielectric layer 311. In addition, a plurality of contacts 312 are formed on the upper surface 311 a and lower surface 311 b of the first dielectric layer 311. Furthermore, the capacitive element 313 is embedded into the first dielectric layer 311 during the fabrication of the inductive element 314 and the interconnection 315 to let the capacitive element 313 and the inductive element 314 electrically connect to the corresponding contacts 312 through the interconnection 315 respectively.

FIGS. 7A to 7C are cross-sectional views schematically showing a fabricating process of the interposer structure 310 shown in FIG. 5B, which includes the following sub-steps. First, referring to FIG. 7A, a plurality of first sub-contacts 312 a, a first sub-dielectric layer 311 c, and a first sub-interconnection 315 a are formed on the first electronic component 320, wherein the first electronic component 320 is electrically connected to the first sub-interconnection 315 a through the first sub-contacts 312 a. The first sub-contacts 312 a are disposed between the first sub-dielectric layer 311 c and the first electronic component 320 and the first sub-interconnection 315 a is disposed on and in the first sub-dielectric layer 311 c. (Not shown)

Next, referring to FIG. 7B, the capacitive element 313 is disposed onto the first sub-dielectric layer 311 c. Then, an etching process is performed on the capacitive element 313 to define the capacitor surface area.

As shown in FIG. 7C, a plurality of second sub-contacts 312 b, a second sub-dielectric layer 311 d, a second sub-interconnection 315 b and a inductive element 314 are formed on the first sub-dielectric layer 311 c through the build-up process, wherein the capacitive element 313 and the inductive element 314 are embedded into the second sub-dielectric layer 311 d. The second sub-contacts 312 b are disposed on the second sub-dielectric layer 311 d. The second sub-interconnection 315 b are embedded into the second sub-dielectric layer 311 d and electrically connected to the first sub-interconnection 315 a. The first sub-dielectric layer 311 c and the second sub-dielectric layer 311 d compose a first dielectric layer 311. The first sub-interconnection 315 a and the second sub-interconnection 315 b compose an interconnection 315. The first sub-contacts 312 a and the second sub-contacts 312 b compose the contacts 312. The capacitive element 313 and the inductive element 314 are electrically connected to the corresponding contacts 312 through the interconnection 315 respectively. It should be noted that the permittivity of the first dielectric layer 311 can be smaller than that of the second dielectric layer 313 b of the capacitive element 313 and the inductive element 314 may be disposed surrounding the capacitive element 313.

Then, referring to FIGS. 4 and 5C, step S030 is carried out to dispose a second electronic component 330 on the first dielectric layer 311 and electrically connect the second electronic component to the corresponding contacts 312. To be more specific, the second electronic component 330 is disposed on the second sub-dielectric layer 311 d through the flip chip bonding technology and electrically connected to the second sub-contacts 312 b.

A fabricating method of a packaging structure of another embodiment is illustrated in detail as follows. Referring to FIGS. 4, 8 and 9, wherein FIG. 8 is a flow chart illustrating a fabricating method of a packaging structure according to another embodiment, and FIG. 9 is a cross-sectional view schematically illustrating the steps S020′ shown in FIG. 8. The fabricating method of the packaging structure of the embodiment includes the steps S010′, S020′ and S030′, wherein the steps S010′ and S030′ are identical with the steps S010 and S030, thus the detail is omitted herein.

The difference between the embodiment and the above embodiment of the packaging structure fabricating method is that: the embodiment further provides a resistive module 316 at the step S020′ during the fabrication of the inductive element 314 and the interconnection 315, and makes the resistive module 316 and the capacitive element 313 stack up with each other in order to be embedded into the first dielectric layer 311, wherein the resistive module 316 is electrically connected to the corresponding contacts 312 through the interconnection 315. It should be noted that the above mentioned method of stacking up the resistive module 316 with the capacitive element 313 and to be embedded into the first dielectric layer 311, is performed by first to stack up the capacitive element 313 and the resistive module 316 and then embedded them into the first dielectric layer 311.

FIGS. 10A to 10B are cross-sectional views schematically showing a fabricating process of the resistive module shown in FIG. 9. The fabricating process of the resistive module 316 includes the following sub-steps. First, referring to FIG. 10A, a substrate 316 a is provided. Then, plural electrodes 316 c are formed on the substrate 316 a. Next, referring to FIG. 10B, a resistive thin film 316 b is formed on the substrate 316 a and electrically connected to the electrodes 316 c. Then, a passivation layer 316 d is formed on the substrate 316 a to cover the electrodes 316 c and the resistive thin film 316 b. Furthermore, according to needs, the substrate 316 a can be thinned out to make the thickness of the resistive module 316 complied with the design requirements after the above steps.

A fabricating method of a packaging structure of another embodiment is illustrated in detail as follows. Referring to FIGS. 4, 11 and 12, FIG. 11 is a flow chart illustrating a fabricating method of a packaging structure according to another embodiment. And the FIG. 12 is a cross-sectional view schematically illustrating the steps S020″ shown in FIG. 11. The fabricating method of the packaging structure of the embodiment includes the steps S010″, S020″ and S030″, wherein the steps S010″ and S030″ are identical with the steps S010 and S030, thus the detail is omitted herein.

The difference between the embodiment and the above embodiment of the packaging structure fabricating method is that: the embodiment of the packaging structure only embeds one passive element, the capacitive element 313, into the first dielectric layer 311 at the step S020″.

The embodiment provides a manufacturing method of the packaging structure, which is compatible with the conventional fabricating process and has lower cost. Since the interposer structure does not contain semiconductor substrates, the interposer structure is thinner and smaller in size. Because the capacitive element is located closer to either the first electronic component or the second electronic component, the efficiency is improved when the capacitive element is served as a de-coupling capacitor. The permittivity of the second dielectric layer is higher to attain a higher capacitance. On the other hand, since the permittivity of the first dielectric layer is lower, the parasitic capacitance value of the inductive element is lower and thus has a better Q-factor. The spiral-like inductive element can be disposed surrounding the capacitive element to achieve a high integration density of the passive element of the interposer structure. In addition, the thickness and the size of the interposer structure can be reduced. The capacitive element can be manufactured individually first, and then be embedded into the first dielectric layer. Therefore, the fabricating method can be integrated with the conventional process to decrease the manufacturing cost. The capacitive element and the resistive module can be manufactured individually first, and then be stacked to each other and embedded into the first dielectric layer. Therefore, the fabricating method of the invention can be integrated with the conventional process to decrease the manufacturing cost.

The embodiment has been disclosed above in the embodiments, but is not limited to those. It is known to persons skilled in the art that some modifications and innovations may be made without departing from the spirit and scope of the embodiment. Therefore, the scope of the embodiment should be defined by the following claims. 

1. A fabricating method of packaging structure, comprising: forming a capacitive element; forming a first dielectric layer on a first electronic component by performing a build-up process, forming an interconnection in the first dielectric layer, and forming a plurality of contacts on the upper and lower surfaces of the first dielectric layer, wherein the capacitive element is embedded in the first dielectric layer during the fabrication of the interconnection and the capacitive element is electrically connected to the corresponding contacts through the interconnection; and disposing a second electronic component on the first dielectric layer, wherein the second electronic component is electrically connected to the corresponding contacts.
 2. The fabricating method of the packaging structure as described in claim 1, wherein the capacitive element comprises two conductive layers and a second dielectric layer located among them, in which the permittivity of the first dielectric layer is smaller than that of the second dielectric layer.
 3. The fabricating method of the packaging structure as described in claim 1, further comprising forming an inductive element at the same time of fabricating the interconnection and the inductive element is electrically connected to the corresponding contacts through the interconnection.
 4. The fabricating method of the packaging structure as described in claim 3, wherein the inductive element is disposed surrounding the capacitive element.
 5. The fabricating method of the packaging structure as described in claim 1, wherein the steps of forming the capacitive element includes: providing a metal film; coating a dielectric material on the metal film; and forming an electrode layer on the dielectric material.
 6. The fabricating method of the packaging structure as described in claim 5, wherein the dielectric material includes ceramic slurry.
 7. The fabricating method of the packaging structure as described in claim 5, further comprising performing a thermal treatment process to the dielectric material after coating the same.
 8. The fabricating method of the packaging structure as described in claim 5, further comprising forming a barrier layer on the metal film before coating the dielectric material.
 9. The fabricating method of the packaging structure as described in claim 5, wherein the finished capacitive element is trimmed into a certain size after the electrode layer is formed.
 10. The fabricating method of the packaging structure as described in claim 5, further comprising performing an etching process to the capacitive element to define the surface area thereof after the capacitive element is embedded into the first dielectric layer.
 11. The fabricating method of the packaging structure as described in claim 1, further comprising providing a resistive module at the same time of fabricating the interconnection, and making the resistive module and the capacitive element stacked up with each other and to be embedded into the first dielectric layer, wherein the resistive module is electrically connected to the corresponding contacts through the interconnection.
 12. The fabricating method of the packaging structure as described in claim 11, wherein the capacitive element and the resistive module are stacked up with each other first, and then being embedded into the first dielectric layer together.
 13. The fabricating method of the packaging structure as described in claim 11, wherein the steps of fabricating the resistive module includes: providing a substrate; and forming a resistive thin film on the substrate.
 14. The fabricating method of the packaging structure as described in claim 13, wherein the steps of fabricating the resistive module further includes: forming a plurality of electrodes on the substrate, wherein the resistive thin film is electrically connected with the electrodes; and forming a passivation layer on the substrate to cover the electrodes and the resistive thin film.
 15. The fabricating method of the packaging structure as described in claim 1, wherein the first electronic component is a semiconductor chip or a wafer.
 16. The fabricating method of the packaging structure as described in claim 1, wherein the second electronic component is a semiconductor chip or a wafer. 